Production of Fe-C alloy powders by mechanical alloying was studied. Fe and graphite elemental powder mixtures containing ۰.۸ and ۱.۵wt.% graphite were mechanically alloyed using a planetary ball mill. The structural changes of powder particles during mechanical alloying were studied by x-ray diffractometery, scanning electron microscopy and microhardness measurements. For both compositions, mechanical alloying for ۳۰h resulted in the development of a nanocrystalline structure with a typical grain size of ۱۶nm containing nanoscale size Fe۳C phase. This structure exhibited high microhardness value of the order of ۶۰۰Hv. The powder particles after ۳۰h of milling had a nearly spherical morphology and narrow size distribution. The mean powder particle size for Fe-۰.۸wt.% graphite composition was ۱۵μm, whereas the Fe-۱.۵wt.% graphite composition achieved a smaller particle size with a mean of ۹μm due to higher graphite content.
کلیدواژه ها:
نویسندگان
M. H Enayati
Department of Materials Engineering, Isfahan University of Technology, Isfahan, ۸۴۱۵۶, Iran
M Zakeri
Department of Materials Engineering, Isfahan University of Technology, Isfahan, ۸۴۱۵۶, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :