Poly vinyl chloride/ montmorillonite nanocomposites and metal-catalyzed living radical graft copolymerization methods used for chemical modification of poly viny chloride

سال انتشار: 1387
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,166

متن کامل این مقاله منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل مقاله (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

ICNN02_437

تاریخ نمایه سازی: 27 شهریور 1391

چکیده مقاله:

Poly(vinyl chloride) (PVC) is an extensively used thermoplastic material because of its flame retardance, high chemical resistance, and good performance in respect of mechanical behavior as well as low price. The successful application of clay, especially montmorillonite (MMT), in the preparation of polymer nanocomposite with excellent properties opens a novel approach to improve the performance of PVC. Wang et al. prepared PVC/clay nanocomposites by melt blending of the polymer with an organically modified clay, both in the presence and absence of di(2-ethylhexyl) phthalate (DOP) plasticizer, and found that the tensile strength of the nanocomposite increased as the fraction of clay increased. Yalcin and Cakmak also prepared PVC/clay nanocomposite by melt blending, and found that DOP plasticizer would help the exfoliation and dispersion of clay particles when DOP fraction was suitable. Wan et al. found that the partially intercalated and partially exfoliated MMT/PVC nanocomposite could be obtained by melt blending of PVC with alkyl quaternary ammonium modified MMT. The nanocomposites showed better mechanical properties than pristine PVC. However, the nanocomposites were easy to discolor during processing due to the decomposition of alkyl quaternary ammonium. Gong et al. reported the synthesis and thermal properties of PVC/MMT nanocomposites via in situ intercalative polymerization process. They also confirmed that the presence of the quaternary ammonium in the nanocomposites was responsible for the accelerated degradation of PVC in the initial stage [1,2]. According these methods, we synthesized Poly vinyl chloride/ montmorillonite nanocomposites. In this study, First, graft copolymerization of PVC with monomers such as styrene has been examined to improve the thermal stability of PVC. This graft copolymerization was prepared by atom transfer radical polymerization (ATRP). In these method PVC condensed with toluene in mild condition and brominated with NBS, was used as a macroinitiator. The formation of the graft copolymer was confirmed with GPC, DSC, 1HNMR and FT-IR spectroscopysynthesizes [3,4]. Then, modified Poly vinyl chloride/ montmorillonite nanocomposites was synthesized

نویسندگان

M Abbasian

Payame Noor University of Tabriz, Tabriz-Iran

S Esmaeily Shoja

Islamic Azad University, Bonab branch, Bonab-Iran

M Adeli

Khorram Abad University, Khorram Abad –Iran

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • G. Chen, Journal of Applied Polymer Science, 106, 817-820, 2007. ...
  • A.A. Shokri, Polymer International, 55, i-vi, 2006. ...
  • P. Shoaeifar, M. Abbasian, A. Entezami, Journal of Polymer Reasearch, ...
  • M.Abbasian, A. Entezami, Iranian Polymer Journal, 15, 393-402, 2006. ...
  • نمایش کامل مراجع