Hydration and Engineering Properties of Mechanically-Activated Composite Cement from Processed Steel Slag and Limestone

سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 249

فایل این مقاله در 17 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

JR_IJMSEI-19-1_002

تاریخ نمایه سازی: 16 بهمن 1401

چکیده مقاله:

The aim of the present research work is to evaluate the feasibility of processing and utilizing steel slag in binary and ternary cement blends with limestone. The physical and microstructural properties of binary and ternary composite cements produced by inter-grinding mixtures of ordinary Portland cement clinker, processed steel slag and limestone in a laboratory ball mill with replacement levels varying from ۰ wt.% to ۳۰ wt.% were studied. The effects of processed steel slag and limestone incorporation on density of dry cement mixes and water consistency, setting time and volume stability of fresh and hardened cement pastes were investigated. Also, density, water absorption, total open pore volume (%) and compressive strength of cement mortars were measured. The mix with ۱۵ wt.% limestone and ۱۵ wt.% processed steel slag was selected as a typical ternary cement mix for complementary studies including X-ray diffractometry, thermal gravimetry, Fourier-transform infrared spectroscopy, and scanning electron microscopy analyses. The results show that removal of relatively high metallic content of steel slag increases its grindability for mechanical activation and improves its hydraulic properties effectively and makes it suitable for being recycled in cement industry. The results show that mechanical activation of the cement mixes enhances the poor hydraulic activity of the processed steel slag and compensates the strength loss to some extent. The physical and chemical properties of all studied composite cement mixes comply with ASTM standard specifications, except the compressive strength of the cement mixes at ۲۸-days containing ۲۰ wt.% or higher amounts of limestone ground to the relatively low Blaine specific surface area of about ۳۰۰۰ cm۲/g.

نویسندگان

Mojtaba Hosseini

Department of Chemistry,Firoozabad Branch, Islamic Azad University,Firoozabad,Fars

Ali Allahverdi

School of Chemical EngineeringIran University of Science and Technology (IUST)Narmak ۱۶۸۴۶ - ۱۳۱۱۴Tehran, IRAN

Mohammad Jaafar Soltanian fard

Department Of Chemistry,Firoozabad Branch,Islamic Azad University,Fars, Iran

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :