Synthesis of new polyurethanes based on ۵, ۶, ۷, ۸ – tetrabromo – ۲, ۳ – dihydro – ۱, ۴ – phthalazine dione
محل انتشار: فصلنامه شیمی آلی-فلزی کاربردی، دوره: 2، شماره: 3
سال انتشار: 1401
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 179
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JAOC-2-3_003
تاریخ نمایه سازی: 31 مرداد 1401
چکیده مقاله:
In this work, ۵,۶,۷,۸-Tetrabromo-۲,۳-dihydro-۲,۳-bis(۲-hydroxyethyl)phthalazine-۱,۴-dione is synthesized by the reaction of ۵,۶,۷,۸-tetrabromo-۲,۳-dihydrophthalazine-۱,۴-dione with ۲-bromoethanol in the presence of triethylamine. The obtained monomer was polymerized with different diisocyanates, including hexamethylenediisocyanate (HMDI), tolylene-۲,۴-diisocyanate (TDI), isophoronediisocyanate (IPDI), ۱,۴-phenylene diisocyanate (p -PDI) and ۴,۴'-methylenebis (phenyl isocyanate) (MDI), to obtain polyurethanes. The measured viscosity for these polymers is in the range of ۰.۵-۰.۶ dlg-۱. The structure of the synthesized polymers was analyzed by infrared (IR), ۱H-NMR spectroscopy methods, viscometry measurements, thermal gravimetric analysis (TGA/DTG), as well as elemental analysis. All the polyurethanes showed very good solubility in common aprotic polar solvents. The good solubility of the polyurethanes can be due to presence of bulky pendant group as side group. The inherent viscosity of the polyurethanes in the range of ۰.۵ – ۰.۶ dL/g indicated the relatively high molecular weight. The diol synthesized here is reported for the first time, and data from different spectra analyses were used to confirm the structures of all compounds. Besides, the analysis suggests that not only the synthetized polymers have favorable polymer properties such as acceptable viscosity range and high thermal resistance, but also these polymers, due to the presence of phthalazine nucleus in their structure, may have medical applications as well.
کلیدواژه ها:
نویسندگان
Ommolbanin Gharib
College of Chemistry, Shahrood University of Technology, ۳۶۱۹۹۹۵۱۶۱, Shahrood, Iran
Hossein Nasr-Isfahani
College of Chemistry, Shahrood University of Technology, ۳۶۱۹۹۹۵۱۶۱, Shahrood, Iran
Mohammad Bakherad
College of Chemistry, Shahrood University of Technology, ۳۶۱۹۹۹۵۱۶۱, Shahrood, Iran
Hossein Mighani
Faculty of Science, Department of Chemistry, Golestan University, P.O. BOX ۱۵۵, Gorgan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :