Dissimilar electron beam welding of high temperature titanium alloys
سال انتشار: 1400
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 134
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
INCWI22_043
تاریخ نمایه سازی: 16 فروردین 1401
چکیده مقاله:
Electron beam welding was applied to join dissimilar Ti۵۵/TA۱۵ high temperature titanium alloys. Defect-free joints were obtained. Microstructure observation via optical and electron microscopes showed that FZ consisted of martensite α΄ and acicular α. The HAZ of both Ti۵۵ and TA۱۵ sides consisted of two regions; LT-HAZ consisted of primary α, secondary α and prior β and HT-HAZ mainly composed of martensite α΄ and acicular α. In addition, a characteristic asymmetrical microhardness profile was observed in dissimilar welded joints lower hardness of fusion zone rather than HAZ of both Ti۵۵ and TA۱۵ alloys.Room temperature tensile test results represented slightly weakness of weld metal compared to the Ti۵۵ and TA۱۵ alloys, however, good strength of welded joint at high temperature test results was achieved.
کلیدواژه ها:
نویسندگان
Vahid Esfahani Yeganeh
Institute of Materials and Energy, Iranian Space Research Centre, Isfahan, Iran