Synthesis and characterization of nano SiO4 from rice husk ash by Precipitation method
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 2,265
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CMRCE03_235
تاریخ نمایه سازی: 13 دی 1390
چکیده مقاله:
This work is presented as studies on the preparation of rice husk ash by burning at 777 oC for 3 and 6 h, respectively. Consequently, silica content obtained after heat treatment at 777 oC for 6 h was 981149. of rice husk ash (RHA) which was purified by alkaline extraction method by using 215N sodium hydroxide. Infrared spectral data supported the presence of hydrogen bonded silinol group and the siloxane groups in silica. Subsequently, the RHA was subjected to precipitation method in order to produce nanosilica. The precipitation was done by refluxing silica from RHA in boiling 215N NaOH. X-ray diffractograms and diffraction pattern showed that the obtained products were amorphous nanosilica. The size of the particle is determined from the number averaged particle radius by LPS that show Nanosilica particles which obtained from the rice husk ash were in the agglomerate form which dimension of 17-37 nm.
کلیدواژه ها:
نویسندگان
Majid Monshizadeh
Department of Material Engineering and Metallurgy, Imam Khomeini International University, Ghazvin, Iran
Mohammad Hossein Ahmadi
Department of Chemistry, Imam Khomeini International University, Ghazvin, Iran
Vahid Mohammadi
Department of Chemistry, Imam Khomeini International University, Ghazvin, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :