Production and Characterization of Nano Crystalline Fe۸۵Si۱۰Ni۵ Soft Magnetic Alloys by Mechanical Alloying
محل انتشار: فصلنامه مواد پیشرفته و فرآوری، دوره: 2، شماره: 4
سال انتشار: 1393
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 332
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-2-4_004
تاریخ نمایه سازی: 12 مهر 1400
چکیده مقاله:
Abstract There are various methods to produce iron based nano crystalline magnetic alloys. Among these methods, mechanical alloying is one of the most important. In this research, nano crystalline Fe۸۵Si۱۰Ni۵ soft magnetic alloy was synthesized by mechanical alloying. The effect of alloying time on phase constituents and magnetic properties of the produced powders was investigated, by X-ray diffraction (XRD) and alternating gradient force magnetometer (AGFM). The XRD results showed that alloy formation started after ۲ hours of milling. Further milling resulted in the reduction of the grain size and lattice parameter. After ۶۰ hours of milling, the grain size was reduced to ۸ nm. AGFM results showed that magnetic saturation and coercivity depends on the alloying time. Increasing the alloying time, causes the increase of magnetic saturation and decrease of coercivity. Abstract There are various methods to produce iron based nano crystalline magnetic alloys. Among these methods, mechanical alloying is one of the most important. In this research, nano crystalline Fe۸۵Si۱۰Ni۵ soft magnetic alloy was synthesized by mechanical alloying. The effect of alloying time on phase constituents and magnetic properties of the produced powders was investigated, by X-ray diffraction (XRD) and alternating gradient force magnetometer (AGFM). The XRD results showed that alloy formation started after ۲ hours of milling. Further milling resulted in the reduction of the grain size and lattice parameter. After ۶۰ hours of milling, the grain size was reduced to ۸ nm. AGFM results showed that magnetic saturation and coercivity depends on the alloying time.
کلیدواژه ها:
نویسندگان
Arash Dezhsetan
Department of Material Engineering, Najafabad Branch, Islamic Azad University, Isfahan, Iran
Ali Saidi
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
Reza Ebrahimi-Kahrizsangi
Department of Material Engineering, Najafabad Branch, Islamic Azad University, Isfahan, Iran