Fabrication of AA۱۰۶۰/Al۲O۳ Composites by Warm Accumulative Roll Bonding Process and Investigation of its Mechanical Properties and Microstructural Evolution
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 207
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ADMTL-10-4_011
تاریخ نمایه سازی: 18 اردیبهشت 1400
چکیده مقاله:
Recently accumulative roll bonding (ARB) has been used as a novel method to produce particle reinforced metal matrix composites. The accumulative roll bonding as a severe plastic deformation (SPD) rolling procedure aimed at enhancing the mechanical properties of metals and alloys. The process consists in rolling series of overlapped sheets with a thickness reduction ratio (e.g. ۵۰%). In this study, warm accumulative roll bonding (Warm- ARB) process has been used to produce Aluminum Metal Matrix Composite (AMMC: AA۱۰۶۰/-۵% Al۲O۳). AA۱۰۶۰ strips were roll bonded as alternate layers up to ۵ rolling passes with ۳۰۰°C preheating for ۵ minutes before each pass. The microstructure and mechanical properties of composites have been studied after different Warm- ARB passes by tensile test, Vickers micro hardness test and scanning electron microscopy (SEM). The results demonstrated that adding alumina particles into AMMCs improves both the strength and tensile toughness of composites. Moreover, the fracture surfaces of samples after the tensile test have been studied during various ARB cycles by scanning electron microscopy (SEM). Also, the results showed that mechanical properties such as tensile strength and average Vickers micro hardness improved with increasing the number of warm ARB cycles. Also, the elongation and tensile toughness of samples dropped in the primary cycles and improved in continuing with increasing the warm ARB cycles. Finally, warm ARB process would allow producing particle reinforced with good mechanical properties.
کلیدواژه ها:
Fractography ، Mechanical Properties ، Metal-Matrix composites (MMCs) ، Particle-Reinforced composites ، Warm accumulative roll bonding
نویسندگان
M. Heydari Vini
Department of Mechanical Engineering, Mobarakeh Branch, Islamic Azad University, Mobarakeh, Isfahan, Iran
P. Farhadipour
School of Mechanical Engineering, Iran University of Science and Technology Tehran ۱۶۸۴۴, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :