Effect of Carbide Particle Size on the Microstructure, Mechanical properties, and Wear Behavior of HVOF-sprayed WC-17% Co Coatings
محل انتشار: مجله سرامیک های پیشرفته، دوره: 6، شماره: 3
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 190
فایل این مقاله در 14 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ACERPT-6-3_001
تاریخ نمایه سازی: 17 فروردین 1400
چکیده مقاله:
This study investigates the effect of carbide particle size on the microstructure, mechanical properties, and abrasive wear resistance of WC-17%Co HVOF-sprayed coatings. The characteristics of WC-1, WC-2, and WC-3 coatings with carbide sizes of 1 µm, 0.9 µm, and 0.5 µm, respectively, were also investigated. WC-1 coating experienced the maximum carbon loss of 42%, while WC-2 and WC-3 coatings underwent lower carbon losses of 30% and 29%, respectively. The XRD pattern revealed W2C/WC peak ratios of 15.58, 9.14, and 14.96% for WC-1, WC-2, and WC-3 coatings, respectively. The Vickers microhardness of WC-1, WC-2, and WC-3 coatings was measured as 1418 ± 61, 1306 ± 71, and 1203 ± 57 kgf/mm2, respectively. The WC-2 coating showed the maximum fracture toughness of 5.9 MPa.m1/2, after which WC-3 and WC-1 coatings were characterized by 5.6 and 5.4 MPa.m1/2, respectively. The wear rate of the coatings abraded by alumina 60 was 1.2-7.8 times higher than that of the coatings abraded by silica 70 almost over the whole range of applied loads (19.6-127.5 N). The WC-3 coating exhibited lower abrasive wear resistance against alumina 60 than WC-1 and WC-2 coatings. The worn surfaces produced by alumina 60 abrasive showed indications of grooving, pitting, and cutting of the coatings’ surfaces. For all coatings abraded by silica 70, removal of the matrix, micro-grooving, carbide particles fragmentation, and voids formation through carbide pullout were detected. For WC-3 coating, in contrast to WC-2 and WC-3, the indications of sub-surface cracking were identified when abraded by both alumina 60 and silica 70.
کلیدواژه ها:
نویسندگان
S. M. Nahvi
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :