Synthesis of CaO nano particles via precipitation in ethanol
محل انتشار: اولین کنفرانس ملی علوم و فناوری نانو
سال انتشار: 1389
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 2,122
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
NNTC01_057
تاریخ نمایه سازی: 8 آبان 1389
چکیده مقاله:
Nanosized CaO powder was prepared via sol–gel precipitation in ethanol followed by a washingdrying treatment and calcination. The reactant concentration, the molar ratio of reactants and the calcinations temperature were inspected by homogenous design. TEM, XRD and SEM were used to characterize the products. The experimental results showed that ethanol can avoid hard agglomerate during precipitation and that calcinations temperature was the major factor to determine the surface area, the diameter and the phase composition of the final product. When the calcina)on temperatures were controlled between 686–1029 °C, the agglomerate-free nano-sized CaO particles with a size range of 5–9 nm were obtained
کلیدواژه ها:
نویسندگان
SSalar Meshkat
Iran, Urmia, Urmia University of Technology, Chemical Engineering Facaulty
H.R. Gholami
Iran, Urmia, Urmia University of Technology, chemical Engineering Facaulty
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :