Microcrystalline Cellulose as a Reinforcing Agent in Wood Plastic Composites
محل انتشار: دومین کنفرانس بین المللی کامپوزیت
سال انتشار: 1389
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,878
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
COMPOSIT02_100
تاریخ نمایه سازی: 24 مهر 1389
چکیده مقاله:
Microcrystalline cellulose (MCC) / Polypropylene (PP) / composites were prepared containing polypropylene-graft-maleic anhydride (PP-g-MA) as compatibilizer. The weight ratio of the cellulosic materials to polymer matrix was 40:60 (w:w). The obtained results showed that tensile, flexural and impact strengths of the composites were significantly enhanced with addition of MCC, as compared with pure PP and composites without MCC. The effect of MCC on impact was minimal compared to the effects of PP-g-MA content. Scanning electron microscopy has shown that the composite, with compatibilizer, promotes better fiber–matrix interaction. In all cases, the degradation temperatures shifted to higher values after addition of PP-g-MA. The maximum improvement on the thermal stability of the composites was achieved when 5% PP-g-MA was used. However, the increase in MCC content substantially reduced the thermal stability. This work showed that MCC along with wood flour could be effectively used as reinforcing agent in thermoplastic matrix
کلیدواژه ها:
نویسندگان
A Nourbakhsh
Assistant Professor, Department of Wood and Paper Science
A Ashori
Assistant Professor, Department of Chemical Technologies
M Kouhpayehzadeh
Faculty Member of Islamic Azad University, Pishva Branch, Varamin, Iran
A Kargarfard
Assistant Professor, Department of Wood and Paper Science, Research Institute of Forests and Rangelands (RIFR), Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :