A Study of the Effect of TPU and Clay Nanoparticles on the Mechanical Behavior of PBT-Based Nanocomposites
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 457
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_MACS-4-3_001
تاریخ نمایه سازی: 14 تیر 1399
چکیده مقاله:
In this research, thermoplastic polyurethane (TPU) and clay nanoparticles were incorporated into poly (butylene terephthalate) (PBT) to improve the impact and tensile properties. The PBT/TPU (90/10, 80/20 and 70/30) samples were prepared by melt mixing using a co-rotating twin-screw extruder followed by injection molding. At the next stage, clay nanoparticles of different weight fractions were added to the PBT/TPU (80/20) blend in the same way to prepare nanocomposite samples. SEM images illustrated good compatibility between TPU and PBT. To characterize the dispersion of clay layers in the polymer matrix, wide-angle X-ray diffraction (WAXD) inspections were performed. The results of the mechanical assessments showed that the addition of TPU to PBT significantly increased the impact strength but decreased the tensile strength and modulus. Incorporating clay nanoparticles into the PBT/TPU blend noticeably improved the tensile properties of PBT/TPU-based nanocomposites. A balance of the tensile and impact properties was found in the PBT/TPU/clay (80/20/3) nanocomposite system.
کلیدواژه ها:
نویسندگان
Ata Chalabi Tehran
Department of manufacturing engineering, Faculty of mechanical engineering, University of Tabriz, Tabriz, ۵۱۳۶۸, Iran
Karim Shelesh-Nezhad
Department of manufacturing engineering, Faculty of mechanical engineering, University of Tabriz, Tabriz, ۵۱۳۶۸, Iran
Pouya Faraji Kalajahi
Department of manufacturing engineering, Faculty of mechanical engineering, University of Tabriz, Tabriz, ۵۱۳۶۸, Iran
Ali Olad
Faculty of chemistry, University of Tabriz, Tabriz, ۵۱۳۶۸, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :