Mechanical Characteristics and Failure Mechanism of Nano-Single Crystal Aluminum Based on Molecular Dynamics Simulations: Strain Rate and Temperature Effects
محل انتشار: فصلنامه مکانیک جامد، دوره: 9، شماره: 4
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 283
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JSMA-9-4_008
تاریخ نمایه سازی: 12 اسفند 1398
چکیده مقاله:
Besides experimental methods, numerical simulations bring benefits and great opportunities to characterize and predict mechanical behaviors of materials especially at nanoscale. In this study, a nano-single crystal aluminum (Al) as a typical face centered cubic (FCC) metal was modeled based on molecular dynamics (MD) method and by applying tensile and compressive strain loadings its mechanical behaviors were investigated. Embedded atom method (EAM) was employed to represent the interatomic potential of the system described by a canonical ensemble. Stress-strain curves and mechanical properties including modulus of elasticity, Poisson’s ratio, and yield strength were determined. Furthermore, the effects of strain rate and system temperature on mechanical behavior were obtained. It was found that the mechanical properties exhibited a considerable dependency to temperature, but they hardly changed with increase of strain rate. Moreover, nucleation and propagation of dislocations along the plane of maximum shearing stress were the mechanisms of the nanocrystalline Al plastic deformation.
کلیدواژه ها:
نویسندگان
R Rezaei
Faculty of Mechanical Engineering, Shahrood University of Technology, Shahrood, Iran
H Tavakoli-Anbaran
Faculty of Physics, Shahrood University of Technology, Shahrood, Iran
M Shariati
Department of Mechanical Engineering, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :