Optimization of an ecofriendly coating containing chitosan and gelatin as corrosion inhibitor of carbon steel grade E by Response Surface Method
محل انتشار: فصلنامه علوم و فناوری ذرات، دوره: 5، شماره: 1
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 403
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JPST-5-1_003
تاریخ نمایه سازی: 3 دی 1398
چکیده مقاله:
Corrosion can lead to tremendous defects, and several approaches are applied to alleviate the destructive consequences. In this study, two chitosan and gelatin biopolymers with glutaraldehyde applied as a cross-linker were used to cover the surface of carbon steel grade E. Results showed that a cross-linker decreased water and ions from reaching the metal surface; thereby, increased the stability of the coating. The experiment design was performed with Design-Expert 7.0.0 software and Response Surface Method (RSM) was used to optimize the concentration of chitosan, gelatin and glutaraldehyde. The coatings quality was investigated with microscopic image. Results showed that the optimum coating consist of 10 g.L-1 chitosan, 5 g.L-1 gelatin and 1 mL.L-1 glutaraldehyde. Electrochemical Impedance Spectroscopy (EIS) test were done to compare the anti-corrosion property. The results demonstrated that this optimized coating can enhance the corrosion resistance of coated carbon steel up to 6 times. This can be attributed to a homogenous uniform coating on the metal surface confirmed with EIS. The scanning Electron Microscope (SEM) showed coating covered pores and scratches of bare coupon and the Atomic Force Microscope (AFM) corroborated the coverage of this composition on the carbon steel surface.
کلیدواژه ها:
نویسندگان
Seyedeh Neda Mousavi
Malek Ashtar University of Technology, Tehran, Iran
Ali Bahrami
Malek Ashtar University of Technology, Tehran, Iran
Minoo Sadri
Malek Ashtar University of Technology, Tehran, Iran
Amin Alipour
Malek Ashtar University of Technology, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :