Nanostructured Palladium-Doped Silica Membrane Layer Synthesis for Hydrogen Separation: Effect of Activated Sublayers
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 459
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJHFC-6-1_001
تاریخ نمایه سازی: 30 آذر 1398
چکیده مقاله:
Palladium doped silica membranes were synthesized by the sol-gel method using two different procedures. The first palladium-doped silica membrane (M1) was synthesized with a coating of four layers of silica-palladium sol. The second membrane (M2) was synthesized with a coating of two silica layers followed by a coating of two silica-palladium layers. Scanning electron microscopy (SEM) proved the formation of uniform γ-alumina interlayers on the supports. SEM results for M1 showed that synthesis of a membrane with this procedure leads to the formation of crack on the membrane selective layer. Single gas permeation measurements of H2 and N2 were carried out at room temperature, 100 °C and 550 °C. Gas permeation results revealed that Knudsen diffusion was dominant in permeation of these gases through membrane M1 while the dominant mechanism in permeation of gases through membrane M2 was activated transport which has exhibited different behavior in comparison with M1. This result is due to the activated sublayers of membrane M2. In this case, H2 permeance increases and N2 permeance decreases with increasing temperature, leading to better separation perforamce of membrane M2 over M1 in separation of H2. Therefore, using the activated silica sublayer in the synthesis of M2 can be used as a high potential method to synthesize a selective palladium-doped silica membrane.
کلیدواژه ها:
نویسندگان
Masoud Majidi Beiragh
Nanostructure Material Research Center, Sahand University of Technology, Tabriz, Iran
Ahmad Gholizade Atani
Nanostructure Material Research Center, Sahand University of Technology, Tabriz, Iran
Nesa Rafia
Nanostructure Material Research Center, Sahand University of Technology, Tabriz, Iran
Ali Akbar Babaluo
Nanostructure Materials Research Center (NMRC)
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :