Solidification Microstructure of In-situ Fe-TiC Hard Coating Synthesized by Laser Surface Treatment

سال انتشار: 1398
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 389

فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

IMES13_123

تاریخ نمایه سازی: 13 آبان 1398

چکیده مقاله:

Laser manufacturing is currently a hot area of research. Synthesis of hard coatings on commercial substrates, such as carbon steel, was the subject of several researches in previous decades. In this study, a new method was applied for in-situ synthesis of Fe-TiC composite coating. The TiC particles were produced by laser surface treatment of a precursor of ilmenite and graphite powders. The powder blend was mechanically activated to make the laser reduction of ilmenite possible. Variations of solidification conditions resulted in formation of a series of microstructures, from the substrate to surface. Gradients of size, morphology and distribution of particles were observed. Moreover, by progress of solidification front various microstructures were developed in the matrix, including planar, cellular, dendritic and eutectic growths. Some new microstructural aspects were also detected. Microhardness measurements verified that the formation of a graded microstructure resulted in appropriate properties

نویسندگان

Arman Khalili

Master of materials science and engineering, Iran University of Science and Technology, Tehran, Iran

Milad Mojtahedi

Assistant Professor, Department of Materials and Textile Engineering, Razi University, Kermanshah, Iran

Massoud Goodarzi

Associate Professor, School of metallurgy and materials engineering, Iran University of Science and Technology, Tehran, Iran

Mohammad Javad Torkamany

Assistant Professor, Iranian National Center for Laser Science and Technology, Tehran, Iran