Developing of Corrosion Resistance Nano Copper Oxide Coating on Copper using Anodization in Oxalate solution
محل انتشار: ماهنامه بین المللی مهندسی، دوره: 31، شماره: 3
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 287
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-31-3_007
تاریخ نمایه سازی: 10 آذر 1398
چکیده مقاله:
Copper alloys are widely used in the manufacturing of heat transfer applications, this due to their excellent heat transfer properties. Copper contamination is one of the serious industrial problems in the boiler feed water system. This contamination commonly resulted from copper corrosion reactions in boiler feed water environment. The best way to reduce the copper contamination is by improving copper corrosion resistance. This research studies the developing of copper corrosion resistant by using anodization technique. The anodization experiments are conducted in oxalate solutions of concentrations from 0.1 to 0.5 M, at a temperature range from 24 to 0 ο C and applied potential from 7.5 to 9 V. Anodized coating analyzed using Field emission scanning microscope, energy dispersive X-ray spectroscopy, and X-ray diffraction. Characterization results referred to the formation of copper oxide anodized coating with grain size range from 25 to 68 nm. The corrosion resistance of the anodized copper samples carried out in simulated boiler feed water. Results show that the corrosion resistance of the anodized samples was enhanced. The corrosion protection efficiencies for the anodized coating increased 86.2% and 74.5% in testing solutions contains 3.5% NaCl, and 2 mg/l NH3, respectively.
کلیدواژه ها:
نویسندگان
Farag I. Haider
Manufacturing and Material Engineering, International Islamic University Malaysia (IIUM).
Muataz Hazza Faizi. AL hazza
Manufacturing and Material Engineering, International Islamic University Malaysia (IIUM).
suryanto suryanto
Manufacturing and Material Engineering, International Islamic University Malaysia (IIUM).
mahmood hameed mahmood mahmood
Manufacturing and Materials Engineering, iium