Thermal Degradation and the Morphology of Chlorosulfonated Polyethylene/Nanoclay Nanocomposites
محل انتشار: نشریه متدهای شیمیایی، دوره: 3، شماره: 2
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 451
فایل این مقاله در 16 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_CHM-3-2_003
تاریخ نمایه سازی: 20 مهر 1398
چکیده مقاله:
The interaction in the nanoclay is expected to be improved as the result of the amalgamation of hypalon chlorosulfonated polyethylene rubber (CSM) with nanoclay in the presence of compatibilizer agent nature rubber (ENR). Melt intercalation method was also applied to prepare CSM phases. The effect of ENR and nanoclay on the mixture behavior was also detected by scanning electron microscopy (SEM). Thermogravimetric analysis (TGA) contributed to scrutinize the thermal properties of the prepared NR/CSMs. The outcomes of the X-ray diffraction study are compatible with those of thermal analysis. The results indicated that CSM was infixed into nanoclay. Regarding the fact that the amount of the nanoclay content was lower than 12 wt%, Flynn-Wall-Ozawa (F.W.O) and Kissinger–Akahira–Sunose (K.A.S.), methods were applied to specify the energy of the apparent activation of the nano/hypalon systems holding 3, 6, 9 wt% of nano. The upshots demonstrated that increasing the thermal stability of hypalon was directed into boosting the nanoclay content. This divulges that there is an interplay between nanoclay, ENR and hypalon. Comparing to micro-filled ENR/CSM and ENR/CSM cross linked systems, it is predicted to conclude an enhanced thermal stability, higher values of Tg, better dispersion the nanoclay and more polish without any cracks.
کلیدواژه ها:
نویسندگان
Hamid Reza Ali-Asgari Dehaghi
Department of Polymer Engineering, South Tehran Branch, Islamic Azad University, ۱۷۷۷۶۱۳۶۵۱, Tehran, Iran
Hamed Jabbari
Department of Polymer Engineering, South Tehran Branch, Islamic Azad University, ۱۷۷۷۶۱۳۶۵۱, Tehran, Iran
Mohammad Reza Kalaee
Department of Polymer Engineering, South Tehran Branch, Islamic Azad University, ۱۷۷۷۶۱۳۶۵۱, Tehran, Iran
Saeedeh Mazinani
New Technologies Research Center (NTRC), Amirkabir University of Technology, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :