The Effect of Cooling Rate on the Solutionizing of IN718 Superalloy Produced via Selective Laser Melting (SLM) Method
محل انتشار: مجله مواد دوستدار محیط، دوره: 3، شماره: 1
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 591
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JEFM-3-1_003
تاریخ نمایه سازی: 25 تیر 1398
چکیده مقاله:
In the present study, IN718 super alloy was produced by selective laser melting (SLM) method and was imposed under solution heat treatment at temperature of 1040°C for 2 hours. Three different environments, such as water, air and furnaces were used to cool the samples after complete solution. The results of microstructural studies conducted by optical microscopy (OM) and field emission scanning electron microscopy (FESEM) showed that intermetallic precipitates were formed during the process, disappear after solution. In order to complete the FESEM results, X-Ray diffraction (XRD) test showed that in at all cooling rates, the only remaining phases of matrix are the austenite (γ) and carbides, which their locations are between the grains according to the microscopic images. This issue indicates the proper selection of solution parameters and proper execution of solution process. The micro hardness test showed that doing solution treatment to reduce the volume fraction or completely remove the secondary phase leads to decreased hardness. By increasing cooling rate, the hardness of samples was reduced, so that the hardness of sample chilled in 30 % water was reduced compared to the sample before the heat treatment.
کلیدواژه ها:
IN718 Superalloy ، Selective Laser Melting (SLM) ، Solution Heat Treatment ، Microstructure ، Hardness
نویسندگان
H. H. Dastgerdi
Iran University of Industries and Mines (IUIM), Tehran, Iran
M. O. Shabani
Department of Mining and Metallurgical Engineering, Amirkabir University of Technology, Tehran, Iran
Y. Shajari
Institute of Materials and Energy, Meshkin Dasht, Karaj, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :