Effect of the FSW Tool Pin Profile on Mechanical Properties of the Al6061-Cu Plates Joint
محل انتشار: مجله مواد دوستدار محیط، دوره: 2، شماره: 1
سال انتشار: 1397
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 554
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JEFM-2-1_002
تاریخ نمایه سازی: 25 تیر 1398
چکیده مقاله:
In current research, the Friction Stir Welding (FSW) technique was used to create a metallurgical joint between Al 6061 plates and Cu meat core. The plates were welded using single pass weld with the rotational speed of 1000 rpm and arc travel speed of 30 mm/ min using different tool pin profiles of cylinder, triangle, and hexagonal. After the rolling process and reaching to 1.7 mm of thickness, to evaluate whether there was no separation in layer plates, the radiography test was applied. For more investigation of the created metallurgical bond, optical microscopy (OM) and scanning electron microscopy (SEM) were used. Studies on the welded samples showed a perfect metallurgical bonding. The bonding thickness between Al plates and the Cu meat sample in the samples with pin profiles of triangle, cylinder and hexagonal shape were estimated to be 30, 39 and 45 µm, respectively. Moreover, in comparison to the FSW samples with triangle and cylinder pin profile, the microhardness and ultimate tensile stress were higher in the FSW samples using hexagonal pin profile. It was owing to the fact that hexagonal pin profile had a larger contact area compared with the other two pins. Therefore, the mechanical work using hexagonal pin was more, resulting in an increase in the hardness and tensile stress. In addition, material flow in the bonding zone increased and contributed to an increase in the width of the joint area
کلیدواژه ها:
نویسندگان
F. khalili
Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
K. Amini
Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
M. Golzar Shahri
Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
F. Gharavi
Department of Materials Engineering, Sirjan Branch, Islamic Azad University, Sirjan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :