Ordered nanoporous carbon (CMK-3) coated fiber for solid-phase microextraction of benzene and chlorobenzenes in water samples
سال انتشار: 1397
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 348
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_AET-4-1_002
تاریخ نمایه سازی: 22 تیر 1398
چکیده مقاله:
Nanoporous carbons (CMK-3) were prepared and have been used as a fiber coating for headspace solid phase microextraction (HS-SPME). The prepared materials were characterized by Scanning Electron Microscopy (SEM), X-Ray Diffraction (XRD) and N2 adsorption/desorption isotherms. The efficiency of the fiber was evaluated using a gas chromatography (GC) system for the extraction of benzene (B) and chlorobenzenes (CBs) from the headspace of aqueous samples. The prepared nanomaterial was coated onto a copper wire for fabrication of the SPME fiber. These fibers featured advantages like easy and fast preparation, high thermal and mechanical stability. To optimize different parameters which influence the extraction efficiency such as sample volume, extraction temperature, extraction time, ionic strength and stirring rate, a Taguchi OA16 (45) orthogonal array experimental design was used. Based on the results obtained from the analysis of variance (ANOVA), the optimum conditions for extraction were established as: 12 mL sample volume; laboratory temperature; 20 % (w/v) NaCl; 35 min extraction time and stirring rate of 600 rpm. Under the optimized conditions for B and CBs, the linearity was from 2.5 to 800 µg/L, the relative standard deviation (RSD %) of the method was between 5.2 and 9.3% and limit of detections (LODs) was between 0.09 and 0.28 µg/L. The recovery values were from 85.40% to 104.20 % in water samples. Finally, the applicability of the proposed method was evaluated by the extraction and determination of B and CBs in the water samples.
کلیدواژه ها:
نویسندگان
Mansoor Anbia
Research Laboratory of Nanoporous Materials, Faculty of Chemistry, Iran University of Science and Technology, Tehran, Iran
Naser kakoli khataei
Research Laboratory of Nanoporous Materials, Faculty of Chemistry, Iran University of Science and Technology, Tehran, Iran
Samira Salehi
Research Laboratory of Nanoporous Materials, Faculty of Chemistry, Iran University of Science and Technology, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :