Fundamental understanding of crystallization mechanism of laser alloyed tool steel
سال انتشار: 1384
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,307
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICME07_109
تاریخ نمایه سازی: 6 آذر 1388
چکیده مقاله:
The objective of the present work was to study the modification of the microstructure of hot-work tool steel X40CrMoV5-1 during the surface modifying by means of laser technology. The aim of such treatment was to harden and alloy the steel surface which had been previously coated with tungsten carbide (WC). Development of the surface layer was observed in which one can distinguish the remelted zone, heataffected zone and the transient zone. The fine grained, dendritic structure occurs in the remelted and alloyed zone with the crystallization direction connected with the dynamical heat abstraction from the laser beam influence zone. The fine grained martensite structure is responsible for hardness increase of the alloyed layer. It has the important cognitive significance and gives grounds to the practical employment of these technologies for forming the surfaces of new tools and regeneration of the used ones.
کلیدواژه ها:
نویسندگان
L.A Dobrzański
Dr H.C. Prof. DSc. PhD. MSc. Eng., Full Professor, Silesian University of Technology, Gliwice, Poland
M Bonek
PhD. MSc. Eng, Assistant Professor, Silesian University of Technology, Gliwice, Poland
E Hajduczek
PhD. MSc. Eng, Assistant Professor, Silesian University of Technology, Gliwice, Poland
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :