Role of Electroless Plating in the Production of W-Cu EDM Electrodes
سال انتشار: 1386
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,483
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICME08_139
تاریخ نمایه سازی: 27 آبان 1388
چکیده مقاله:
Tungsten - copper (W-Cu) electrodes have been used widely to machine die steel and tungsten carbide work-pieces owing to high thermal conductivity of Cu, and the better spark erosion resistance, low thermal expansion coefficient and high melting temperature of W. In present study, tungsten particles with average size of 8μm were used to electroless coating of Ni and Ni-P. The compacting pressure and sintering temperature were adjusted for powder to attain the desired skeleton density forproducing W-15Cu. Then the skeletons were infiltrated with oxygen-free copper at 1300 C in hydrogen. As coated powder and compacts were characterized by EDS analysis, scanning electron microscopy (SEM) and optical microscopy. Also measurement of density and electrical resistivity were performed. Results showed, infiltration process improves in case of coated powders and higher values in density are observed. In case of coated powders, relative density and electrical resistivity of compacts increase as the amount of Ni in coating increases to about 1%Wt. In higher values of Ni relative density is approximately constant, but electrical resistivity increases as the amount of additive and P in composition increases.
کلیدواژه ها:
نویسندگان
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :