Influence of carbon nanotube and graphene oxide on the properties of copper matrix composite produced by powder metallurgy
محل انتشار: ششمین کنفرانس بین المللی متالورژی پودر
سال انتشار: 1397
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 475
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
PMAUTO06_069
تاریخ نمایه سازی: 23 آذر 1397
چکیده مقاله:
Copper matrix composites have been used in spot welding electrodes for the automotive assembly and sliding electrical contact applications. In this study, two types of copper matrix composites powder reinforced with Carbon Nano Tube (CNT) and Graphene Oxide (GO) were prepared using high energy ball milling. The subsequent consolidation process of resulting powder was done by cold and hot press sintering at different conditions. For this purpose, the copper powder with different percentages of CNT and GO (1 wt.%) was mechanically ball milled for 5 hours. Then, discs with 10 mm diameter and 10 mm thickness were prepared by the cold press under pressure of 165 MPa . Also, compacts were processed by hot-pressing at 500 °C under the pressure of 165 MPa . Under the same conditions as compacts processed from milled composite powders, compacts from 5 hours milled pure electrolytic copper powders were also synthesized for comparison. Subsequently, these samples were sintered at 800 °C for 1 hour under argon atmosphere. The samples characterized by X-ray diffraction, optical and scanning electron microscopy. The microstructure, density and mechanical properties of samples have been studied. Microstructure analysis results have proved that homogeneous microstructure was formed after the consolidation process. The results showed that increases in GO and CNT percentage caused to increase in hardness of samples. Also, the hardness of hot pressed sample was more than that of cold pressed one. Also, the Cu-GO composites have higher density and hardness.
کلیدواژه ها:
نویسندگان
F. Zarei
School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran.
M. Balavar
School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran.
S. Sheibani
School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran.