Influence of interlayer thickness on diffusion brazing behavior of Al2024/AZ31 system: experimental and simulation
سال انتشار: 1396
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 424
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CMME01_010
تاریخ نمایه سازی: 5 آذر 1397
چکیده مقاله:
Diffusion brazing of Al2024 to AZ31 was carried out using Sn-based interlayer with thickness of 20, 40, 60 and 80 µm. SEM micrographs from joint zones showed that although Sn interlayer uniformly and continuously wetted the parent metals, some micro-cracks appeared in the joint brazed with 80-µm thick interlayer. The FEM simulation indicated that the joint strength increased with enhancement of interlayer thickness from 20 to 60 µm. This event was due to the increase of loading capacity with the rise in interlayer thickness. The decrease in shear strength from 60 to 80 µm interlayer thickness can be attributed to the concentration of stress in the interlayer during shear strength test. The trend of experimental results for shear strength test was also similar to the FEM outcomes.
کلیدواژه ها:
نویسندگان
Emadoddin Abaei
Department of Materials Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran
Mohammad Kazemi Nasrabadi
Department of Aerospace Engineering, Shahid Sattari University of Aeronautical engineering, Tehran, Iran