Prediction of microstructure and mechanical properties of X70 pipeline steel welded joint via hardness mapping
سال انتشار: 1396
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 420
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CMME01_009
تاریخ نمایه سازی: 5 آذر 1397
چکیده مقاله:
The aim of this work is to study the effects of preheating and type of electrodes on microstructure and mechanical behaviors of X70 pipeline steel welded joint. The results indicated an accordance among the hardness measurements, the microstructure and the tensile strength. It is also found that hardness mapping detected coarse and fine grain subzones in the heat affected zone which were not identified by optical micrographs. The impact test showed that the non-preheated sample, welded by cellulosic E8010, had the minimum value of toughness which was due to the hydrogen assistance cracking. The fractography results revealed that the size and uniformity of strengthening phases (Ti,V,Nb) (C,N) affected mechanical properties of welded joints.
کلیدواژه ها:
نویسندگان
Ali Amirnasiri
Faculty of Mining and Materials Engineering, Amirkabir University of Technology (AUT), ۴۲۴ Hafez Ave., Tehran, ۱۵۹۱۶۳-۴۳۱۱, Iran
Arjang Hamdollahzadeh
Faculty of Mining and Materials Engineering, Amirkabir University of Technology (AUT), ۴۲۴ Hafez Ave., Tehran, ۱۵۹۱۶۳-۴۳۱۱, Iran