EFFECT OF GLASS FIBER ON SHRINKAGE AND MECHANICAL PROPERTIES OF HIGHLY FLOWABLE CEMENT PASTE
محل انتشار: نخستین کنفرانس بین المللی بتن
سال انتشار: 1388
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,991
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCT01_158
تاریخ نمایه سازی: 19 شهریور 1388
چکیده مقاله:
Self-consolidating concrete (SCC) is a new class of high-performance concrete that can spread readily into place under its own weight and fill restricted sections as well as congested reinforcement structures without the need for mechanical consolidation and without undergoing any significant separation of material constituents due to its unique flow behavior. SCC mix design often involves the use of high paste volume and low coarse aggregate content, thus leading to relatively high shrinkage and higher cracking potential compared to conventional concrete. The use of fibers depending on the fiber type and fiber content may considerably increase the toughness, energy absorption capacity, reduce cracking, improve the impact resistance and durability of cement composites. One of the most important properties regarding the design and the durability of structures is shrinkage which seems to be increased for highly flowable cement paste (HFCP). Glass ber reinforcement can be an excellent solution for shrinkage, bending and tensile resistance problems of HFCPs. This research focuses on the development of shrinkage in highly flowable cement paste, which plays an important role in shrinkage of SCC, reinforced with glass fibers. five cement paste mixtures were prepared containing 0, 0.1, 0.2, 1 and 2 percent of 6 mm long glass fibers (with aspect ratio of 150). The effect of fiber content on total shrinkage of the cementitious material is investigated in this research using shrinkage curves over 240 days. Besides, the rheological properties of fresh fiber reinforced cement paste are investigated by mini-slump test and the 28 days compressive and flexural strength of the mixtures are determined. Test results indicated that Synergistic effects resulting from fibers with optimum volume fraction allow to develop HFCP in which Excellentechanical properties can be obtained without jeopardizing the flow properties.
کلیدواژه ها:
نویسندگان
N.A Libre
۱Department of Civil Engineering, Islamic Azad University, Qazvin branch, Barajin St, Qazvin, Iran
I Mehdipour
۲Concrete Research Center, Department of Civil Engineering, Islamic Azad University, Qazvin branch, Qazvin, Iran
A Alinejad
۲Concrete Research Center, Department of Civil Engineering, Islamic Azad University, Qazvin branch, Qazvin, Iran
N Nouri
۲Concrete Research Center, Department of Civil Engineering, Islamic Azad University, Qazvin branch, Qazvin, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :