Investigation of the Cathodic Electrodeposition Effect on the Phosphate Layer, on Steel, Galvanized Steel and Electrogalvanised Steel Substrates
محل انتشار: دومین کنفرانس بین المللی رنگ و پوشش خودرویی
سال انتشار: 1388
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,848
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICAPC02_019
تاریخ نمایه سازی: 22 تیر 1388
چکیده مقاله:
Phosphate layer which is used for corrosion resistance improvement in automotive industry, is affected by protective layers applied after that. To make better knowledge of this changing, the effect of voltage and processing time of CED on the phosphate layer was investigated with three types of substrates; i.e. steel, galvanized steel and electrogalvanised steel. The substrates were initially phosphated and then electrodeposited under different voltages and time. The electrodeposited layer was then removed from the substrates by solvent and changes of the phosphate layer was studied. The phosphate layer was characterized by determination of phosphate layer coating weight and SEM technique. Atomic absorption spectroscopy was used to investigate the influence of electrodeposition process on degree of dissolution of different crystals in processing bath. Also the salt spray test was carried out to study the corrosion resistance of electrodeposited film upon changes of the phosphate layer.The results showed that the highest extent of phosphate layer dissolution in CED process respectively obtained on the steel, galvanized steel and electrogalvanised steel substrates. In contrast, the salt spray test showed that the galvanized steel results in highest corrosion resistance, followed by electrogalvanized and carbon steel.
کلیدواژه ها:
نویسندگان
N Akbarzadeh
Khosh Paint and Resin producing company
M. R. M. Attar
AmirKabir university of Technology
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :