One Step Rapid Synthesis of Nano-Crystaline ZnO by Solution Combustion Method
محل انتشار: سومین کنگره بین المللی رنگ و پوشش
سال انتشار: 1388
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 2,001
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCC03_082
تاریخ نمایه سازی: 6 اردیبهشت 1388
چکیده مقاله:
In this study nano-crystaline ZnO particles were synthesized by microwave-assisted solution combustion method. For this purpose, zinc nitrate and urea were used as oxidation agent and fuel respectively. In order to study the effect of fuel oxidizer ratio on powder properties different urea/nitrate ratios; 0.25, 0.50, 0.75 and 1 were used. X-ray Diffractometer, Scanning Electron Microscopy and Fourier transform infra red were used for powders characterization. The results have shown that ZnO phase was formed after combustion reaction for f/o 0.5, 0.75 and 1. Calcinations step have increased the crystalinity level of the samples. The crystallite size was calculated by Sherer formula and was in the range of 28-32 nm. The micrograph by SEM has shown that for f/o 0.75 and 1 particles were agglomerated and partially sintered.
کلیدواژه ها:
نویسندگان
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :