The Effect of Zirconia and Ceria Nanoparticles in the Hybrid Nanocomposites Coatings on the Copper Corrosion Protection
محل انتشار: سومین کنگره بین المللی رنگ و پوشش
سال انتشار: 1388
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 2,132
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCC03_046
تاریخ نمایه سازی: 6 اردیبهشت 1388
چکیده مقاله:
Sol-gel processes are widely used in the preparation of environmental friendly hybrid nanocomposite coatings. In our pervious studies, the hybrid silica based nanocomposite coatings have been investigated for corrosion protection of 1050 aluminum alloys and the effect of silica content in the hybrid composition was also studied. In this study, the hybrid sols were prepared by hydrolysis and condensation of 3-glicidoxypropyl-trimethoxysilane (GPTMS) in the presence of an acidic catalyst, Bisphenol A (BPA) as cross-linking agent and 1 methyl imidazol as iniatiator. Additionally, the various ratios of ceria and zirconia nanoparticles was doped in the hybrid sol. The metal substrates were coated by spin coatings technique. The shape and size of the nano particles in the hybrid films were observed and determined using a transmission electron microscopy (TEM). The chemical composition and the structure of the nanocomposite hybrid coatings were studied by X-ray photoelectron spectroscopy and scanning electron microscopy (SEM), respectively. The evolution of the corrosion protection roperties of the hybrid coatings was studied by EIS (electrochemical impedance spectroscopy), which can provide quantitative information on the role of the different pretreatments.
کلیدواژه ها:
نویسندگان
A Ershad-Langroudi
Resin & Surface Coatings (CRSC)
D Zare-Hossein-abadi
Iran Polymer and Petrochemical Institute
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :