Co3O4 spinel protection coating for solid oxide fuel cell interconnect application
سال انتشار: 1393
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 541
فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJHFC-1-2_007
تاریخ نمایه سازی: 21 فروردین 1397
چکیده مقاله:
In the present study, electrophoretic deposition (EPD) method in different electric fields (30 – 300 V/cm) was used to apply Co3O4 spinel coating to SUS 430 as SOFC interconnect. The coated and uncoated specimens were pre-sintered in air at 800 and 900 °C for 3 h followed by cyclic oxidation at 700 and 800 °C for 500 h, respectively. X-ray diffraction analysis (XRD), Scanning Electron Microscope (SEM) and Energy Dispersive Spectroscopy (EDS) were used for characterization of the prepared samples. The results indicated that the electric field of 100 V was an effective voltage to obtain crack-free coating. A comparison between the oxidation resistance of coated and uncoated specimens indicated that the weight change of the coated specimen was larger than that of the uncoated one during the cyclic oxidation, so the Co3O4 coating is not effective for improving the oxidation resistance. According to the obtained results, the oxidation rate constant (Kp) for the coated specimens at 700 and 800°C inair were 2.36×10-14 and 3.37×10-12 gr2 cm−4 s−1, respectively.
کلیدواژه ها:
نویسندگان
Reza Irankhah
Department of Ceramic, Materials and Energy Research Center, Tehran, ۱۴۱۵۵-۴۷۷۷, Iran
Babak Raissi
Department of Ceramic, Materials and Energy Research Center, Tehran, ۱۴۱۵۵-۴۷۷۷, Iran
Amir Maghsoudipour
Department of Ceramic, Materials and Energy Research Center, Tehran, ۱۴۱۵۵-۴۷۷۷, Iran
Abdullah Irankhah
Hydrogen and Fuel Cell Research Lab, Chemical Engineering Department, University of Kashan, Kashan, ۸۷۳۱۷-۵۱۱۶۷, Iran