Joining ceramics to metals by a newly designed Cu-base active filler alloy
سال انتشار: 1396
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 535
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES11_336
تاریخ نمایه سازی: 7 اسفند 1396
چکیده مقاله:
A new active filler alloy was developed to join the ceramics to metals by a single-stage route. Metallization is rarely used nowadays due to containing many stages and high costs. Brazing is the most used method to join such a connection. Most researchers have used Ag-Cu-Ti filler alloys to join ceramic materials to ceramics or metals. These silver-based alloys have high costs due to the presence of Ag element. Therefore, a Cu-base active filler alloy with a chemical composition of Cu-20.5% Sn- 20% Ag- 3.5% Ti was developed using the phase diagrams and thermodynamic rules. XRD, EDS, SEM and DSC analyses were performed to evaluate the developed filler alloy. It was concluded that the Cu41Sn11 intermetallic was the most destructive phase in the alloy. An MMC composite was joined to the copper to study the mechanical properties of the resultant joint. The highest tensile strength obtained 140 MPa for Cu-1.1% Al2O3 – Cu joint. Also, the wetting angles of the filler alloy on the composite were measured by the drop test where the lowest wetting angle obtained as 10°.
کلیدواژه ها:
نویسندگان
Farzad Habibi
PhD candidate of Materials Science and Engineering, Sahand University of technology
Ahad Samadi
Associate professor of Materials Science and Engineering, Sahand University of technology,
Parvaneh Farshbaf
PhD candidate of Materials Science and Engineering, Sahand University of technology,