Effect of Electroless Plating Conditions on Ni-Sn-P Coatings, Properties
سال انتشار: 1396
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 489
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES11_329
تاریخ نمایه سازی: 7 اسفند 1396
چکیده مقاله:
In this study, the electroless Ni-Sn-P coatings with different compositions were deposited on the copper substrate. To investigate the effect of plating condition on Ni-Sn-P coatings, properties, time (20-40 minute) and temperature of electroless plating (80-88℃) were changed. Surface composition and surface morphology of coatings were studied by Energy Dispersive Spectroscopy (EDS) and Field Emission Scanning Electron Microscope (FESEM) respectively. Corrosion behavior of coatings was studied by electrochemical tests in 10 wt % acid sulfuric. Results showed that changes in time and temperature of electroless plating led to changes in Ni, Sn, P contents, deposition rate, and surface morphology of coatings. Coatings that obtained at higher times and temperatures of electroless plating showed a nodular structure with bigger nodule size. Results of corrosion behavior tests in 10 wt % acid sulfuric showed that coating with higher tin content had the best corrosion behavior.
کلیدواژه ها:
نویسندگان
Mahnaz Yaghoobi
Master of corrosion engineering Faculty of materials engineering, Sahand University of technology, Tabriz, Iran
Naghi Parvini Ahmadi
Professor of materials science and engineering, Faculty of materials engineering, Sahand University of technology, Tabriz, Iran
Parvaneh Asl Farshbaf
Master of corrosion engineering, Sahand University of Technology, Faculty of materials engineering, Sahand University of technology, Tabriz, Iran