Effects of Zr element and Solidification Parameters on the microstructure and tensile properties of Al-7%Si-0.5%Mg Alloy
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 466
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IIAC04_063
تاریخ نمایه سازی: 22 دی 1396
چکیده مقاله:
In this investigation, experiments were carried out to study the relationship of master alloy Al–5Zr and solidification parameters in Al-7wt%Si-0.5wt%Mg casting with various thicknesses under the same solidification condition. The optimum level of Zr as Al–5Zr grain refiner was found to be ( 0.03 wt.%), respectively. It was found that 0.03 wt% Zr addition could refine the microstructure significantly and modify the eutectic Si from plate-like morphology to fiber converted. The results show that the Increasing cooling rate through reduced sections, decreases grain size and dendrite arm spacing ,but Zr-refined specimens showed lowest sensitivity to cooling rate. The relationships between the microstructre and cooling rate have investigated. The microstructural characterization was carried out by optical microscopy and image analysis. meachanical properties also have investigated at various thicknesses.
کلیدواژه ها:
نویسندگان
Omid Marjani
M.sc.student, department of Metallurgy and Materials south Tehran branch, Islamic Azad University, Tehran, Iran
Masoud Emamy
Professor,School of Metallurgy and Materials, College of Engineering, University of Tehran, Tehran, Iran
Bita Pourbahari
M.sc.student ,School of Metallurgy and Materials, College of Engineering, University of Tehran, Tehran, Iran