A Short-time Hydrothermal treatment for Synthesis of Nanoporous Faujasite Membranes
محل انتشار: همایش بین المللی ژئولیت ایران
سال انتشار: 1387
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 2,202
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ZEOLITE01_208
تاریخ نمایه سازی: 30 دی 1387
چکیده مقاله:
High quality faujasite membranes were prepared using hydrothermal treatments. Tubular Porous Mullite
Supports were fabricated from Kaolin clay by a temperature-programmed calcination treatment, following a
leaching treatment. As observed in SEM photographs, the porosity of the support increased during the
leaching treatment. The NaX faujasite zeolite powders were prepared hydrothermally and characterized with
XRD and SEM. The best crystalline powder and the corresponding starting gel were respectively used for
seeding treatment and hydrothermal crystallization of a thin, continuous and fully covering X-type zeolitic
top layer on outer surface of the cylindrical support. The membrane was characterized with XRD and SEM.
کلیدواژه ها:
نویسندگان
m Asghari
Research Laboratory for Separation Processes, Faculty of Chemical Engineering, Iran
t Mohammadi
Research Laboratory for Separation Processes, Faculty of Chemical Engineering,
m Fouladi
Research Laboratory for Separation Processes, Faculty of Chemical Engineering, Iran
R. F. Alamdari
Department of Chemistry and Chemical Engineering, Faculty of Material and Chemical Engineering,
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :