DISCONTINUOUS DYNAMIC RECRYSTALLIZATION DURING ACCUMULATIVE BACK EXTRUSON OF A MAGNESUMALLOY
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 480
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_274
تاریخ نمایه سازی: 10 تیر 1396
چکیده مقاله:
The study of nucleation mechanism of new grains during severe plastic deformation of magnesium alloys is of greatimportance to control the characteristics of final microstructures. To investigate the role of discontinuous recrystallization, a wrought AZ31 magnesium alloy was deformed by accumulative back extrusion process at 330 °C. The obtained microstructures were studied using optical and field emission microscopy as well as electron back scattered diffraction techniques. The results demonstrated that the fine and ultrafine grains formed along the prior grain boundaries yielding a bimodal structure. The EBSD analysis showed that the new grains exhibit a similar basal texture to deformed grains, which may confirm the operation of strain induced boundary migration mechanism.
کلیدواژه ها:
نویسندگان
S.M. FATEMI-VARZANEH
School of Metallurgical di Materials Eng., University of Tehran, North Karegar Tehran, Iran
AZARE HANZAKI
School of Metallurgical de Materials Eng, University of Tehran, North Karegar Tehran, Iran
R. VAGHAR
School of Metallurgical di Materials Eng., University of Tehran, North Karegar Tehran, Iran
A. CHALAYAMOLY
School of Metallurgical & Materials Eng., University of Tehran, North Karegar Tehran, Iran