PALLADIUMMEMBRANE FABRICATION ON SLCA NANOPOROUS FLMIALUMNA SUPPORT
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 412
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_234
تاریخ نمایه سازی: 10 تیر 1396
چکیده مقاله:
Nanoporous layer with high chemical and mechanical strength is very attractive in hydrogen purification. In this study, dense palladium coating was fabricated on macroporous O-alumina using nanoporous silica thin film as surface modifier. The silica film has been prepared by an acid catalytic sol-gel process under the action of CTAB template. TEOS was starting material and homogeneous, clear transparent solution was prepared and coated on O-alumina disk by dip-coating. Then heated slowly (1 C/min) to 400°C in air. Pd layer deposited electrolessly on it. Surface morphology of silica film and palladium layer have been studied by AFM and SEM. There is shown silica inorganic nanoscale walls produced between ordered surfactant micells. palladium layer that shows the grains of palladium grains is about 10pm which leads to formation of a relatively dense film.
کلیدواژه ها:
نویسندگان
MOHAMMAD AMIR SAADATINASAB
Department of Chemistry, Faculty of Science, Tarbiat Modares University, P.O Box ۱۴۱۱۵-۱۷۵ Tehran, Iran
HUSSEN GHARIBI
Department of Chemistry, Faculty of Science, Tarbiat Modares University, P.O. Box ۱۴۱۱۵-۱۷۵ Tehran, Iran
ALDIREZA ZOLFAGHARI
Department of Physical Chemistry, Chemistry and Chemical Research of Iran, Tehran, Iran
FARHAD GOLMOHAMMADI
Department of Chemistry, Faculty of Science, Tarbiat Modares University, P.O. Box ۱۴۱۱۵-۱۷۵ Tehran, Iran