Effects of comonomer content on thermal stability of insitu polymerized POM

Polyoxymethylene (POM) is an engineering plastic with unique properties such as chemical resistance that has poor thermal stability. Therefore by using comonomer the thermal stability of POM will be improved. In this study insitu cationic copolymerization of 1, 3, 5-trioxane (TOX) as monomer and 1, 3-dioxolane (DOX) as a comonomer in presence of phosphotungstic acid as a catalyst during reactive melt blending toward POM was investigated. POM samples were characterized by FTIR to study the chemical structure, DSC for investigation of the crystallinity and, TGA to study the thermal degradation were carried out. Test results shows that copolymer sample (TOX / DOX: 95/5 composition) had greater thermal stability than the others

کلیدواژه ها:

Polyoxymethylene ، reactive blending ، 1 ، 3 ، 5-trioxane(TOX) ، 1 ، 3-dioxolane(DOX) ، phosphotungstic acid