Effect Of Pulsed Nd:YAG Laser Welding Parameters On Weld Pool Dimension And Microstructure Of SA508 Gr.4N Low Alloy Steel
محل انتشار: دهمین همایش مشترک و پنجمین کنفرانس بین المللی انجمن مهندسی مواد و متالورژی و انجمن علمی ریخته گری ایران
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 446
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES10_421
تاریخ نمایه سازی: 6 اردیبهشت 1396
چکیده مقاله:
Similar welding of SA508 Gr.4N low alloy steel by pulsed Nd:YAG laser beam welding equipment was investigated. This steel has special application in energy industries and gas turbine components. Due to high capacity of laser welding compare to traditional methods in reducing defects and problems related to the heat-affected zone, in this study the effect of laser welding parameters on weld pool size, microstructure and optimum joint parameters based on the importance and impact of heat input on depth and width and welding defects were investigated. The results of welding microstructure observed by optical and scanning electron microscopy. The optimum heat input is specified. According to the results of metallographic images fusion zone and heat affected zone microstructure is fine martensitic and results of hardness in weld width show increasing in hardness of this area. Also, the fine M23C6 carbides in the martensitic area of fusion zone was observed. Due to high thermal focus of laser welding method, narrow HAZ was observed and hardness in this zone is as hard as weld metal. however, due to thermal gradients in temperature decrease some microstructural orientation can be seen near fusion zone of weld metal.
کلیدواژه ها:
نویسندگان
Kiumars Ahmadpoor
MSc student of material science and engineering (welding) University of Tehran, Iran
Seyed Ali Asghar Akbari Mousavi
Associated professor at department of Metallurgy and Materials Engineering, University of Tehran, Iran
Mehdi Alizadeh
MSc student of material science and engineering (welding) University of Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :