Buttering in Order to Repair Welding of Aged IN-519 Steel

سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 454

فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

IMES10_411

تاریخ نمایه سازی: 6 اردیبهشت 1396

چکیده مقاله:

In present study repair welding was accomplished on heat-resistant cast steel tube IN-519 which was utilized in hydrogen reformer furnace at 871 ◦C for 80000 hours. Gas tungsten arc welding (GTAW) was performed for repairing. Optical microscopy (OM), scanning electron microscopy (SEM) and X-ray diffractometry (XRD) were carried out to study microstructure of the aged specimen. Heat affected zone (HAZ) of specimen selected from radiation zone (the place where torch’s flame are directly in contact with the tube, RZ) had cracks after welding and it is not desirable. In order to prevent cracking in repair welding of brittle zone, buttering was investigated. Buttering with Inconel 82 as filler could almost prevent cracking but it couldn’t be completely effective because of the result in bending test. Mechanical tests were performed in order to investigate the repair quality.

نویسندگان

n Sohrabi

Graduate student at school of metallurgy and materials science

s.f Kashani Bozorg

Associate professor at school of metallurgy and materials science, College of Engineering, University of Tehran, Tehran, Iran

m Sadeghi

Welding Engineer

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • پنجمین کنفرنس بین لمللی مهندسی _ ومتلویی ودهمین کنفرنس‌مشترک فجمن ...
  • J.R. Davis, ed., ASM Handbook of Heat-Resi stat Materials, 1997. ...
  • S. Borjali, S.R. Allahkaram, H. Khosravi, "Effects of working temperature ...
  • P. Yan, Z. Liu, "Toughness evolution of 9Cr-3W-3Ch martensitic heat ...
  • S. Jung, C. Jeon, Y.H. Jo, W.M. Choi, B.J. Lee, ...
  • T. Branza, F. D eschaux-B eaume, G. Sierra, P. Lours, ...
  • L. Milovic, T. Vuherer, I. Blacic, M. Vrhovac, M. Stankovic, ...
  • K.-H. Lee, J.-Y. Suh, S.-M. Hong, J.-Y. Huh, W.-S. Jung, ...
  • S. Shi, J.C. Lippold, _ 'Microstructure evolution during service exposure ...
  • A.K. Ray, S. Kumar, G. Krishna, M. Gunjan, B. Goswami, ...
  • M. Attarian, A.K. Taheri, _ 'Micro structural evolution in creep ...
  • A. Alvino, D. Lega, _ Giacobbe, V. Mazzocchi, A. Rinaldi, ...
  • M. Attarian, A. Karimi Taheri, S. Jalilvand, A. Habibi, _ ...
  • Z.R. Xu, R.B. McLellan, "Hydrogen enhanced diffusional creep", Acta Mater. ...
  • A. Panthee, B. Thapa, H.P. Neopane, "Quality control in welding ...
  • S. Katsas, J. Nikolaou, G. Papadimitriou, _ 'Micro structural changes ...
  • , 9 Nov. 2016 Shiraz University ...
  • , 9 Nov. 2016 Shiraz University ...
  • Y.P. Zhao, J.M. Gong, Y. Jiang, Q.N. Li, X.W. Wang, ...
  • G. Teran, R. Cuamatzi -Melendez, A. Albiter, C. Maldonado, A.Q. ...
  • _ A. Duchosal, F. Deschaux-B eaume, P. Lours, S. Haro, ...
  • T. Branza, _ D eschaux-B eaume, V. Velay, P. Lours, ...
  • C. Zhang, X. Song, P. Lu, X. Hu, "Effect of ...
  • H.. Tawancy, A. UI-Hamid, A.. Mohammed, N.. Abbas, "Effect of ...
  • R. Dehmolaei, M. Shamanian, A. Kermanpur, _ _ Micro structural ...
  • J. Erneman, M. Schwind, P. Liu, J.O. Nilsson, H.O. Andren, ...
  • J.. Colwell, R.L. ; Hoffman, "Weld cracking in Nb modified ...
  • نمایش کامل مراجع