Effect of intercritical annealing time on microstructure and deformation mechanism of high bainite dual phase steels
سال انتشار: 1387
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 2,066
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ISME16_939
تاریخ نمایه سازی: 20 آبان 1386
چکیده مقاله:
In this study, Ferrite-Bainite dual phase structure steels were produced using appropriate heat treatment and according to intercritical annealing holding time dual phase steels with different ferrite volume fraction (Vf) were produced. Samples of these steels with dual phase structure were tensile tested at room temperature. Results showed that the yield strength and work hardening decrease linearly with increasing Vf whilst ductility decreases. It was ascertained that during deformation of these steels at studied Vf range two stage of work hardening take place. Finally variation of mechanical properties and Hollomon equation parameters with differing Vf have been used to rationalize deformation mechanisms activated at different stages of deformation.
کلیدواژه ها:
نویسندگان
Mohammad Reza Akbarpour
Materials & Energy Research Center,Karaj,Iran
Mohammad Farvizi
Materials & Energy Research Center,Karaj,Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :