synthesis and optimization of chitosan ceramic -supported membrane for pervaporation ethanol dehydration
محل انتشار: دومین همایش ملی غشا و فرایندهای غشایی
سال انتشار: 1394
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,021
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
MEMBRANE02_117
تاریخ نمایه سازی: 22 مهر 1394
چکیده مقاله:
In the present work, ceramic-supported chitosan hybrid membranes were prepared for pervaporation dehydration of ethanol. Mullite and combined mullite-alumina (50% alumina content) tubular ceramic supports were fabricated, and their influence on membrane performance was compared to a commercial α-alumina support. The membrane preparation parameters were different ceramic supports and the concentration of chitosan solution (varying from 2 wt.% to 4 wt.%). The supports and hybrid membranes were characterized by field emission scanning electron microscopy (FE-SEM) and contact angle measurement. The results show, with increasing chitosan concentration, permeability decreases and selectivity increases. It was also found that the separation factor decreases with increasing feed temperature and feed water content, while the permeation flux increases. The membrane that was coated on α-alumina support with a 3 wt.% chitosan concenteration exhibited the best pervaporation performance, leading to a permeation flux and separation factor of 352 g.m-2.h-1 and 200 for 90 wt.% ethanol in feed at 60 ºC, respectively
کلیدواژه ها:
نویسندگان
mahdi Nikbakht
School of Chemical Engineering, College of Engineering, University of Tehran, Tehran, Iran.
Sepideh Soroush
Research Center for Membrane Separation Processes, Faculty of Chemical Engineering, Iran University of Science and Technology, Tehran, Iran.
Morteza Asghari
Separation Processes Research Group (SPRG), Department of Engineering, University of Kashan, Kashan, Iran
Mohammad Mehdi Montazer-Rahmati
School of Chemical Engineering, College of Engineering, University of Tehran, Tehran, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :