Using liquid homogenization in order to produce Al-Gr compositewith SPS and cold pressed-sintered in furnace and investigation ofmicrostructure
محل انتشار: چهارمین کنفرانس بین المللی کامپوزیت
سال انتشار: 1393
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 609
متن کامل این مقاله منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل مقاله (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
COMPOSIT04_119
تاریخ نمایه سازی: 22 مهر 1394
چکیده مقاله:
To produce aluminum matrix composite reinforced with graphite particles, mixing of pure aluminum and graphite powders by a new method, called homogenization in liquid phase, was performed. The graphite content was chosen from zero to4.5wt.%. First, the graphite powder was poured into acetone, and was mixed by ultrasonic. The aluminum powder was added to the solution and ultrasonic was continued. Then the filtered mixture was dried in vacuum, with suitable temperature and time.Composite samples were produced using the dried powder by two ways: spark plasma sintering (SPS) and cold pressing and thereafter sintering in a vacuum furnace under different pressure, temperature and time. The microstructure was investigated byOM and SEM. To calculate the porosity and density of the samples the Archimedes method was used. Brinell hardness test were used. Compared to other methods, using this method caused significant improvement in the distribution of graphite particles in thematrix and finally the increasing the hardness .The optimum wt.% of graphite to distribute uniformly in the aluminum matrix and to obtain the highest hardness and lowest prosity was 3wt.%.
کلیدواژه ها:
نویسندگان
H Pakdell Noghabi
Msc. Student, Department of Materials Engineering,Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
A Babakhani
Associate Professor, Department of Materials Engineering,Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
S.A Sajjadi
Professor, Department of Materials Engineering,Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran