Formation of nano-thin TiO2 layer on ceramic support and study the photocatalytic properties
محل انتشار: هفتمین کنگره ملی مهندسی شیمی
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 785
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_494
تاریخ نمایه سازی: 25 فروردین 1394
چکیده مقاله:
Nano-titanium dioxide (TiO2) thin films were fabricated on tubular alumina ceramic support by sol-gel spraying method. The crystalline structure and morphology of the synthesized nano-TiO2 were examined by X-ray diffraction (XRD) and Field Emission Scanning Electron Microscope(FE-SEM), respectively. The adsorptive and photocatalytic activities of the deposited nano-TiO2 films with different number of layers were evaluated by removal of acetaldehyde in air under UVirradiation. The XRD patterns demonstrated that the nano-TiO2 films were well synthesized andcrystallized consisting anatase and rutile, with (101) and (110) planes, respectively. The average crystallite size was determined 16.3 nm using Scherrer equation. The SEM images showed that thecoated nano-TiO2 thin films by spraying sol solution were less agglomerated and more uniformcompared to the TiO2 synthesized powders. Increasing the number of coated layers enhanced the photocatalytic activity of TiO2 in acetaldehyde decomposition
کلیدواژه ها:
نویسندگان
shohreh Fatemi
Corresponding Author: School of Chemical Engineering, University College of Engineering, University of Tehran, Enghelab Street, P.O.Box ۱۱۳۶۵–۴۵۶۳, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :