Equilibrium, kinetic and thermodynamic studies of hydrogen adsorption on multi-walled carbon nanotubes
محل انتشار: هفتمین کنگره ملی مهندسی شیمی
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 635
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_471
تاریخ نمایه سازی: 25 فروردین 1394
چکیده مقاله:
In this study, the quilibrium adsorption of hydrogen on multi-walled carbon nanotubes (MWCNT) were experimentally investigated using volumetric method in a dual sorption vessels at temperature range of 288–318 K and pressures up to 40 bars. The result obtained indicated that the equilibrium uptake of hydrogen by MWCNT rapidly increases with pressure while temperature had a marginal effect on it at the temperature range under study. The maximum storage capacitydid not exceed 3% at the lowest temperature and highest pressure under study. The experimentaldata was well fitted by the Frendlich model isotherm considering the values of regression correlation coefficients. The kinetic study revealed a very fast sorption of hydrogen onto MWCNTadsorbent. The parameters of the pseudo-first-order kinetic model were confidently recovered from a nonlinear fit to the experimental data which indicated the adsorption of hydrogen onto MWCNT was dominated by physisorption. Isosteric heat of adsorption was evaluated from a set ofisotherms based on the Clausius–Clapeyron equation. Results showed that although the adsorption of hydrogen on MWCNT was exothermic, but the heat of adsorption was too low. The kinetic study revealed a very fast sorption of hydrogen onto MWCNT occureded in few seconds. The results emphasized that lower temperature and higher pressure is needed to improve the storage capacity of hydrogen on MWCNT adsorbent
کلیدواژه ها:
نویسندگان
s khalili
Chemical Engineering Department, Babol Noshiravani University of Technology,PO.Box ۴۸۴,Babol, Iran
a.a ghoreyshi
Chemical Engineering Department, Babol Noshiravani University of Technology,PO.Box ۴۸۴,Babol, Iran
m jahanshahi
Chemical Engineering Department, Babol Noshiravani University of Technology,PO.Box ۴۸۴,Babol, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :