Affecting parameters on the microstructural morphology of polysulfone membranes via nonsolvent induced phase separation
محل انتشار: هفتمین کنگره ملی مهندسی شیمی
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 959
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_206
تاریخ نمایه سازی: 25 فروردین 1394
چکیده مقاله:
Flat sheet polysulfone membranes were prepared by phase inversion process. The effect of composition and temperature of coagulation bath and concentration ofpolymer in dope solution on the morphology of membranes were investigated. Changing the bath composition from pure water to the solution with composition of 60/40 (w/w) of NMP and water increased the porosity of top layer and the finger-like macrovoid structure near the support side of the membranes was decreased. The same result observed when coagulation bath temperature increased from 25 °C to 60 °C The morphology of membranes was analyzed by scanning electron microscope and performance of membranes was investigated in terms of pure water permeability and tensile strength. The experimental results show that increasing polymer concentration from 12 to 15 wt%, decreases pure waterpermeability and increases tensile strength. For both polymeric compositions, with increasing of coagulation bath temperature, the tensile strength and pure water permeability of the membranes increased, simultaneously
کلیدواژه ها:
نویسندگان
Parya Amirabedi
Faculty of Chemical Engineering, Sahand University of Technology, Tabriz, Iran . Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran
reza Yegani
Faculty of Chemical Engineering, Sahand University of Technology, Tabriz, Iran . Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran
Hamed Soleymani
Faculty of Chemical Engineering, Sahand University of Technology, Tabriz, Iran . Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :