Effect of cooling bath on LLDPE microporous membrane structure in thermally induced phase separation
محل انتشار: هفتمین کنگره ملی مهندسی شیمی
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 991
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_198
تاریخ نمایه سازی: 25 فروردین 1394
چکیده مقاله:
Thermally induced phase separation (TIPS) is versatile method for making microporous membranes. The purpose of this work is to investigate the coolingbath temperature and type effects on the membrane structure prepared via TIPS method. The morphology of the resulting membrane shows a typical bicontinuous structure. When quenching into water at different temperatures, a larger pore size was obtained at higher temperature. Pore sizes are about 0.7 μm, 1.2 μm, and 2.2 μm for the water cooling bath with 273K, 303K and 333K. Porosity and tensile tests confirm these results. When the composition of the coagulation bath is similar with the diluents, the chemical potential difference of diluents would be declinedand the concentration of diluent in polymer lean phase would be kept constant in stagnant condition which leads the droplets to grow and the pore size of the systemwill be larger. However in water cooling bath, the concentration of diluent in polymer lean phase decreased rapidly and pore size growth is decelerated which result is lower porosity
کلیدواژه ها:
Microporous membrane ، Thermally induced phase separation ، Linear low density polyethylene ، Cooling bath effect
نویسندگان
Elham Shokri
MS.c Student of Chemical Engineering, Sahand University of Technology, Tabriz, Iran Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran
Reza Yegani
Assistant Professor of chemical Engineering of Sahand University of Technology, Tabriz, Iran . Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran
zahra godarzi
Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran
leila noori
Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :