Automotive industry: Using conducting composites as primer coating under the cataphoretic painting

  • سال انتشار: 1393
  • محل انتشار: چهارمین کنگره بین المللی پوشش های حمل و نقل
  • کد COI اختصاصی: ICAPC04_017
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 931
دانلود فایل این مقاله

نویسندگان

A Goodarzi

HMS, Harvard University, Landmark Center

چکیده

Conductive polymer coatings are mostly considered as one of the most effective anti-corrosion materials, while at the same time are the most environmentally friendly materials.The negatively charged water-soluble long, need likemultiwal carbon nanotubes (better known as MWCNT-7) serves as anionic dopant during the electropolymerization to synthesize PPy/MWCNT composite films. The synthetic, morphological and electrical properties of PPy/MWCNT-7 films and polypyrrole (PPy) films were compared. Characterization was performed by cyclic voltammetry and scanning electron microscopy (SEM). SEM images revealed that the incorporation of MWCNT-7 significantly altered the morphology of the PPy. To predict mechanical properties of carbon nanotube composites bonded with multiple multiwall carbon nanotubes, we have used computational method based on molecular dynamics (MD) and molecular mechanics (MM). Therefore, to evaluate the anti-corrosive features of the matrix Polypyrrole (PPy) film, experiments were performed to analyse the performance of PPY and multiwallcarbon nano-tubes (MWCNT-7) or Long, tangled (MWCNTLT) reinforced composite coatings. Computational tools were implemented to investigate mechanical properties of PPy/MWCNT-7 and PPy/MWCNTLTcomposites. Then, using potentiodynamic measurements, transmission electron microscopy (TEM) and scanning electron microscopy (SEM), the obtained films were experimentally assessed as anti-corrosive materials. The SEM/TEM results showed that the MWCNTLTand MWCNT-7 were fully dispersed in the composite coatings, further tests indicated they also have significantly improved mechanical integrity of composites. Furthermore, it was safe to conclude that using composite coating is more capable at anti-corrosion protecting than using pure PPy. Increasing MWCNT content were in parallel of increasing Young’s moduli, and values changed from 2.67 GPa (pure PPy) to 4.15–4.61 GPa (PPy/MWCNT-7 composite system).

کلیدواژه ها

Molecular modelling; Mechanical properties; Corrosion protection

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.