The Effects of Silica Modulus and Aging on Compressive Strength of NaOH-Activated Pumice-Based Geopolymer Composites
سال انتشار: 1392
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,576
فایل این مقاله در 13 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCAU01_0267
تاریخ نمایه سازی: 29 تیر 1393
چکیده مقاله:
The environmental impact of Portland cement is significant. In the procedure of cement production, production of one ton cement releases about one ton CO2 in environment. To enhance material greenness and produce alternative binders as a geopolymer, the physical and mechanical properties of Hasankale based pumice geopolymer has been discussed in this study and to identify the best geopolymer mix ratios, varying silica modulus, water/binder (w/b) and Na2O content have been investigated via trial and error approach. Hence nine series of geopolymer pastes differing in Na2O content (4%, 7% and 10%), silica modulus (0.52, 0.6 and 0.68) and w/b ratios (0.36, 0.40 and 0.44) were manufactured to activating Hasankale based ground pumice in this study. The test results indicated that the mix with MS=0.68, Na2O=0.10%, w/b=0.36 gave the higher compressive strength approximately 40 MPa. These test results indicated that the produced Geopolymers compressive strength were high enough and can be used as a structural material. Turkey is one of the richest countries in terms of pumice resources in the world. Regarding to the reduction of necessary energy to produce Portland cement, it is expected to have economic benefit too.
کلیدواژه ها:
نویسندگان
Mehrzad Mohabbi Yadollahi
Department of Civil Engineering, Atatürk University, ۲۵۲۴۰, Erzurum, Turkey
Ramazan Demirboğa
Department of Civil Engineering, Atatürk University, ۲۵۲۴۰, Erzurum, Turkey Engineering Faculty, Civil Engineering Department, King Abdulaziz University, Jeddah, Saudi Arabia
Rıza Polat
Department of Civil Engineering, Atatürk University, ۲۵۲۴۰, Erzurum, Turkey
Alireza Motamadnia
Department of Civil Engineering, Azarshar branch, Islamic Azad University, Tabriz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :