Leaching Kinetics of Stibnite in Sodium Hydroxide Solution
محل انتشار: ماهنامه بین المللی مهندسی، دوره: 27، شماره: 2
سال انتشار: 1392
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 856
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-27-2_008
تاریخ نمایه سازی: 17 خرداد 1393
چکیده مقاله:
The leaching kinetics of stibnite in basic solution has been investigated. Spherical pellets of antimony sulphide were dissolved in 1 molar sodium hydroxide solutions at different temperatures. It was foundthat the shrinking core with ash layer model could satisfactorily explain the dissolution process. Usingthis model, it was found that initially the rate controlling step was a chemical reaction with activation energy of 10.2 kJ/mol. As the ash layer built up, diffusion through the ash layer became the rate controlling step. The activation energy for this step was found to be 33.4 kJ/mol. It was also observedthat smaller particle size, larger solid to liquid ratio, and higher NaOH solution concentrations resulted in higher concentrations of stibnite in the leach solution
کلیدواژه ها:
نویسندگان
a dodangeh
Department of Materials Science and Engineering, Sharif University of Technology, Tehran, Iran
m halali
Department of Materials Science and Engineering, Sharif University of Technology, Tehran, Iran
m hakim
Department of Materials Science and Engineering, Sharif University of Technology, Tehran, Iran
m.r Bakhshandeh
Department of Materials Science and Engineering, Sharif University of Technology, Tehran, Iran